Molybdenum metal & alloys

News Group

Molybdenum metal & alloys

Issue Time:2018-12-04

Molybdenum metal & alloys

Molybdenum  metal is usually produced by powder metallurgy techniques in which Mo powder is hydrostratically compacted and sintered at about 2100°C. Hot working is done in the 870-1260°C range. Moly forms a volatile oxide when heated in air above about 600°C and therefore high temperature applications are limited to non-oxidizing or vacuum environments.

Moly alloys have excellent strength and mechanical stability at high temperatures (up to 1900°C). Their high ductility and toughness provide a greater tolerance for imperfections and brittle fracture than ceramics.

The unique properties of molybdenum alloys are utilised in many applications:

  • High temperature heating elements, radiation shields, extrusions, forging dies, etc;
  • Rotating X-ray anodes used in clinical diagnostics;
  • Glass melting furnace electrodes and components that are resistant to molten glass;
  • Heat sinks with thermal expansivity matching silicon for semiconductor chip mounts;
  • Sputtered layers, only Ångstroms (10-7 mm) thick, for gates and interconnects on integrated circuit chips;
  • Sprayed coatings on automotive piston rings and machine components to reduce friction and improve wear.

For specialised applications, Mo is alloyed with many other metals:

  • Mo-tungsten alloys are noted for exceptional resistance to molten zinc;
  • Mo is clad with copper to provide low expansion and high conductivity electronic circuit boards;
  • Mo-25% rhenium alloys are used for rocket engine components and liquid metal heat exchangers which must be ductile at room temperature.